Mechanical Type Vertical Vibration Tester
Scope of application:
Used for measuring wear resistance, pilling performance and surface changes of woven fabrics, knitted fabrics, woven fabrics, coated fabrics and non-woven fabrics.
Parametri tecnici
| Number of stations | 9 bits | Counting range | 0 ~ 999999 volte |
| Maximum dynamic range | horizontal: 60.5 + 0.5mm vertical: 24 + 0.5mm | Pressure quality | UN, gripper: 198 + 2 2G
B, material specimen weight: 395 + 2 2G C.Sample weight of furniture decoration: 594 + 2 2G D, B type clamping device: 155, plus or minus 1 G E, stainless steel butterfly plate: 260 + 1G |
| Effective friction diameter of grinding block | Tipo A. 198 G (1.96 N) friction head Φ 28.65 + / – 0.05 mm
Friction type B 155 G (1.52 N) Φ 90 + / – 0.10 mm |
The relative movement speed of the clamping device and the grinding table | 50 + 2giri/min(30-70r/min adjustable) |
| Quality of sample weight | 2385 + 10G | External dimension | 850 X 650 x 350mm |
| Alimentazione elettrica | Ac220V 50Hz 500W | Peso | 150kg |
Mechanical Type Vertical Vibration Tester
Norma di prova :
Wear-resisting: GB/T 21196.2, GB/T 13775, ISO 12947, ISO 17704, ISO 5470-2, ASTM D4966, iws-tm 112, Che cavolo 2543, Che cavolo 3424-24, Che cavolo 5690, Che cavolo 8428, M, P19, Prossimo 18, SN 198529, TWC 112, JIS L1096
Pilling: GB/T 4802.2, ISO 129+ 45-2, ASTM D4970, IWS TM 196, M, P17, Next TM26, SN 198525
Mechanical Type Vertical Vibration Tester
Test mode:
Mode 1: the circular sample and the same material fabric are rubbed by li sha, such as Lissajous graphic movement trajectory, and then, after the specified number of revolutions, the grading of the sample starting pilling will be evaluated.The principle corresponds to the test of the degree of pilling of the fabric with standard requirements.(24 * 24 mm)
Modello 2: round fabric sample under certain pressure, and standard abrasive according to Li Sha as (Lissajous) and track curve of friction each other, cause the sample damaged, expressed as a sample broken wear-resisting times wear-resisting performance of fabric.The principle corresponds to the test of wear resistance of the fabric.(60 * 60 mm)
Pattern 3: circular fabric sample under certain pressure, and standard abrasive friction each other in a straight line trajectory for, cause the sample damaged, expressed as a sample broken wear-resisting times wear-resisting performance of fabric.The principle corresponds to the test of wear resistance of the fabric.(100 mm)