BGD 564 Penguji Mandrel Silinder

Keterangan

BGD 564Cylindrical Mandrel Tester

BGD 564 Penguji Mandrel Silinder complies with ISO 1519：2011，ASTM D522 and DIN 53152.It is used to assess the resistance of a coating of paint, varnish or related product to cracking and/or detachment from a metal or plastic substrate when subjected to bending round a cylindrical mandrel under standard conditions.

This tester consists of three PVC rolls wich are arranged side by side and run on pivoting bearings. Thus, the coating is not exposed to damge or shear stress during the test.

Tes dapat dilakukan：

— baik sebagai tes “lulus/gagal”., dengan melakukan pengujian dengan satu mandrel ukuran tertentu, untuk menilai kepatuhan terhadap persyaratan tertentu;

— atau dengan mengulangi prosedur menggunakan mandrel yang lebih kecil berturut-turut untuk menentukan diameter mandrel pertama yang lapisannya retak dan/atau terlepas dari substrat..

BGD 564Cylindrical Mandrel Tester

Parameter teknik

■ Latest and humanization design, convenient and quick to operate.
■ 12 pcs stainless steel mandrels with different diameters：Φ2、Φ3、Φ4、Φ5 、Φ6 、Φ8 、Φ10 、Φ12 、Phi 16 、 Φ20 、Φ25 、Φ32mm

■ All mandrels are machined precisely by high hardness stainless steel, 2mm and 3mm mandrels are done by hardening treatment, it won’t be deformed even bend the thick test panels.

■ Suitable test panels size：Length 120mm～150mm；widith ≤80mm；thickness ≤1.0mm

■ Come with Calibration Certification
■ meminta informasi：BGD 564—Penguji Mandrel Silinder

BGD 564Cylindrical Mandrel Tester

BGD 564 Penguji Mandrel Silinder complies with ISO 1519：2011，ASTM D522 and DIN 53152.It is used to assess the resistance of a coating of paint, varnish or related product to cracking and/or detachment from a metal or plastic substrate when subjected to bending round a cylindrical mandrel under standard conditions.

This tester consists of three PVC rolls wich are arranged side by side and run on pivoting bearings. Thus, the coating is not exposed to damge or shear stress during the test.

Tes dapat dilakukan：

— baik sebagai tes “lulus/gagal”., dengan melakukan pengujian dengan satu mandrel ukuran tertentu, untuk menilai kepatuhan terhadap persyaratan tertentu;

— atau dengan mengulangi prosedur menggunakan mandrel yang lebih kecil berturut-turut untuk menentukan diameter mandrel pertama yang lapisannya retak dan/atau terlepas dari substrat..